Advanced Study on Synthesis and Optical Performances of a Waterborne Polyurethane-based Polymeric Dye | Chapter 05 | Emerging Trends in Engineering Research and Technology Vol. 1

A waterborne polyurethane-based polymeric dye (WPU-CFBB) was synthesized by anchoring 1, 4-bis(methylamino)anthraquinone (CFBB) to waterborne polyurethane chains. The number molecular weight, glass transition temperature and average emulsion particle size for the polymeric dye were determined, respectively. This polymeric dye exhibited intriguing optical behaviors. The polymeric dye engendered two new absorption bands centered at about 520 nm and 760 nm if compared with CFBB in UV-vis spectra. The 760 nm peak showed hypsochromic shift with the decrease of average particle sizes. The polymeric dye dramatically demonstrated both hypsochromic and bathochromic effects with increasing temperature. The fluorescence intensity of the polymeric dye was much higher than that of CFBB. It was found that the fluorescence intensities would enhance from 20°C to 40°C and then decline from 40°C to 90°C. The fluorescence of the polymeric dye emulsion was very stable and was not sensitive to quenchers.

Author(s) Details

Xianhai Hu
CAS Key Laboratory of Soft Matter Chemistry, Department of Polymer Science and Engineering, University of Science and Technology of China, Hefei 230026, P.R. China and School of Materials and Chemical Engineering, Building Energy Efficiency Research Institute, Anhui University of Architecture, Hefei 230022, P.R. China.

View Books: http://bp.bookpi.org/index.php/bpi/catalog/book/147

Leave a Reply

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out /  Change )

Google photo

You are commenting using your Google account. Log Out /  Change )

Twitter picture

You are commenting using your Twitter account. Log Out /  Change )

Facebook photo

You are commenting using your Facebook account. Log Out /  Change )

Connecting to %s